Flexible electrochromic windows: a comparison using liquid and solid electrolytes

Abstract

In the present work, two electrochromic devices (or electrochromic windows) based on intrinsically conducting polymers were assembled and characterized. For both devices, the materials used on the assembling were the same except for the electrolyte layer. In the first, we used as electrolyte a propylene carbonate solution and in the second the elastomer poly(epichlorohydrin-co-ethylene oxide), both containing LiClO4. The conductivity of the liquid electrolyte (10-3 S cm-1) is approximately two orders of magnitude higher than for the solid electrolyte and we obtained very good electrochromic properties in both cases. The calculated electrochromic efficiency at 640 nm was 700 C cm-2 for the liquid electrolyte device and 360 C cm-2 for the solid state device. Solid state electrochromic windows have been investigated and some of its advantages over windows with liquid electrolytes are discussed.

Translated abstract

Neste trabalho foram montados e caracterizados dois dispositivos eletrocrômicos (ou janelas eletrocrômicas) utilizando como materiais opticamente ativos polímeros instrinsecamente condutores. Os materiais usados na montagem foram os mesmos, exceto pelo eletrólito usado. No primeiro foi usado como eletrólito uma solução de carbonato de propileno e no segundo o elastômero poli(epicloridrina-co-oxido de etileno), ambos contendo LiClO4. A condutividade elétrica do eletrólito líquido é aproximadamente duas ordens de grandeza maior (10-3 S cm-1) do que a do eletrólito sólido e foram obtidos excelentes resultados do ponto de vista eletrocrômico em ambos os casos. A eficiência eletrocrômica em 640 nm foi calculada em 700 C cm-2 para o dispositivo com eletrólito liquido e 360 C cm-2 para o dispositivo montado com eletrólito sólido. O uso de dispositivos eletrocrômicos de estado sólido tem chamado bastante atenção e suas vantagens são discutidas.