For the first time, porous carbon microfibers co-doped with N/P/K were synthesized from cane molasses by combination of electrospinning and carbonization techniques and its electrochemical application to electrode materials for supercapacitors was investigated.
In this study, we demonstrate a simple and low cost method to synthesize N/P/K co-doped porous carbon microfibers (CMFs) from a sugar-rich byproduct (cane molasses) as the precursor material. A two-step method for the synthesis of N/P/K co-doped porous CMFs involving electrospinning of precursor material followed by simple carbonization at various temperatures (773.15–1173.15 K) was successfully applied. The N/P/K co-doped porous CMFs exhibited high specific surface area (∼580 m 2 g −1) and hierarchical porous structure. The potential application of N/P/K co-doped porous CMFs as supercapacitor electrodes was investigated in a two-electrode configuration employing aqueous K 2SO 4 solution and ionic liquids/acetonitrile (ILs/ACN) mixtures as the electrolytes. A series of electrochemical measurements include cyclic voltammetry, galvanostatic charge–discharge and cycling durability all confirmed that the CMF-1073.15 supercapacitor exhibited good electrochemical performance with a specific capacitance of 171.8 F g −1 at a current load of 1 A g −1 measured in 1.5 M tetraethylammonium tetrafluoroborate (TEABF 4)/ACN electrolyte, which can be charged and discharged up to a cell potential of 3.0 V. The specific energy density and power density of 53.7 W h kg −1 and 0.84 kW kg −1 were achieved. Furthermore, the CMF-1073.15 supercapacitor showed excellent cycling performance with capacitance retention of nearly 91% after 2500 charge–discharge cycles, characterizing its electrochemical robustness and stable capacitive performance.