The support of bone marrow stromal cell differentiation by airbrushed nanofiber scaffolds.

Abstract

Nanofiber scaffolds are effective for tissue engineering since they emulate the fibrous nanostructure of native extracellular matrix (ECM). Although electrospinning has been the most common approach for fabricating nanofiber scaffolds, airbrushing approaches have also been advanced for making nanofibers. For airbrushing, compressed gas is used to blow polymer solution through a small nozzle which shears the polymer solution into fibers. Our goals were 1) to assess the versatility of airbrushing, 2) to compare the properties of airbrushed and electrospun nanofiber scaffolds and 3) to test the ability of airbrushed nanofibers to support stem cell differentiation. The results demonstrated that airbrushing could produce nanofibers from a wide range of polymers and onto a wide range of targets. Airbrushing was safer, 10-fold faster, 100-fold less expensive to set-up and able to deposit nanofibers onto a broader range of targets than electrospinning. Airbrushing yielded nanofibers that formed loosely packed bundles of aligned nanofibers, while electrospinning produced un-aligned, single nanofibers that were tightly packed and highly entangled. Airbrushed nanofiber mats had larger pores, higher porosity and lower modulus than electrospun mats, results that were likely caused by the differences in morphology (nanofiber packing and entanglement). Airbrushed nanofiber scaffolds fabricated from 4 different polymers were each able to support osteogenic differentiation of primary human bone marrow stromal cells (hBMSCs). Finally, the differences in airbrushed versus electrospun nanofiber morphology caused differences in hBMSC shape where cells had a smaller spread area and a smaller volume on airbrushed nanofiber scaffolds. These results highlight the advantages and disadvantages of airbrushing versus electrospinning nanofiber scaffolds and demonstrate that airbrushed nanofiber scaffolds can support stem cell differentiation.