High-mobility BaSnO3 grown by oxide molecular beam epitaxy

The study of quantum phenomena in semiconductors requires epitaxial structures with exceptionally high charge-carrier mobilities. Furthermore, low-temperature mobilities are highly sensitive probes of the quality of epitaxial layers, because they are limited by impurity and defect scattering. Unlike many other complex oxides, electron-doped SrTiO(3) single crystals show high (approximately 10(4) cm(2) V(-1) s(-1)) electron mobilities at low temperatures. High-mobility, epitaxial heterostructures with SrTiO(3) have recently attracted attention for thermoelectric applications, field-induced superconductivity and two-dimensional (2D) interface conductivity. Epitaxial SrTiO(3) thin films are often deposited by energetic techniques, such as pulsed laser deposition. Electron mobilities in such films are lower than those of single crystals. In semiconductor physics, molecular beam epitaxy (MBE) is widely established as the deposition method that produces the highest mobility structures. It is a low-energetic, high-purity technique that allows for low defect densities and precise control over doping concentrations and location. Here, we demonstrate controlled doping of epitaxial SrTiO(3) layers grown by MBE. Electron mobilities in these films exceed those of single crystals. At low temperatures, the films show Shubnikov-de Haas oscillations. These high-mobility SrTiO(3) films allow for the study of the intrinsic physics of SrTiO(3) and can serve as building blocks for high-mobility oxide heterostructures.

We discovered that La-doped BaSnO3 with the perovskite structure has an unprecedentedly high mobility at room temperature while retaining its optical transparency. In single crystals, the mobility reached 320 cm^2(Vs)^-1 at a doping level of 8x10^19 cm^-3, constituting the highest value among wide-band-gap semiconductors. In epitaxial films, the maximum mobility was 70 cm^2(Vs)^-1 at a doping level of 4.4x10^20 cm^-3. We also show that resistance of (Ba,La)SnO3 changes little even after a thermal cycle to 530 Deg. C in air, pointing to an unusual stability of oxygen atoms and great potential for realizing transparent high-frequency, high-power functional devices.