      Caracterización física y mecánica de compuestos de Guazuma crinita Mart. a base de polipropileno virgen Translated title: Physical and mechanical characterization of Guazuma crinita Mart. composites based on virgin polypropylene

      research-article

      Read this article at

      Bookmark
          There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

          Abstract

          Resumen Se elaboraron materiales compuestos plástico madera con base en partículas de madera de la especie Guazuma crinita (bolaina blanca), proveniente del raleo de 4, 5 y 6 años, con polipropileno virgen (PP), además se utilizó como agente acoplante anhídrido maleíco de polipropileno (MAPP). La producción de probetas se hizo por el método de extrusión, compresión térmica y corte por láser. Las partículas de bolaina blanca se tamizaron con tamaños de malla ASTM: -40/+60, -60/+80 y -80/+100. Las proporciones de mezcla polipropileno/bolaina fueron: 70/30, 80/20 y 90/10. Todas las formulaciones incluyeron 2 % de MAPP como agente acoplante. Se evaluaron las propiedades físicas de contenido de humedad, densidad, absorción e hinchamiento; así como, las propiedades mecánicas de flexión estática, tensión y resistencia al impacto. Para la discusión de resultados se realizó una caracterización anatómica de la fibra (longitud, diámetro, espesor de pared, diámetro del lumen y coeficiente de esbeltez), además de un análisis químico de los componentes de la misma (extractivos, holocelulosa, lignina y cenizas). Los resultados permiten apreciar influencia de la variable proporción de mezcla sobre las principales propiedades físicas, así como de la variable tamaño de partícula respecto a la tensión. La edad de la madera no representó una fuente de variabilidad significativa.

          Translated abstract

          Abstract Wood plastic composite materials based on Guazuma crinita wood particles (White Bolaina) from forestry thinning of 4, 5 and 6 years old and virgin polypropylene (PP) were prepared, using polypropylene maleic anhydride (MAPP) as a coupling agent. Specimens were made by extrusion, thermal compression and laser cutting. White bolaine particles were sieved with ASTM mesh sizes: -40/+60, -60/+80 and -80/+100. Proportions of polypropylene/Bolaina mixture were: 70/30, 80/20 and 90/10. All formulations included 2 % MAPP as a coupling agent. Physical properties as moisture content, density, absorption and swelling were assessed, as well as the mechanical properties of static bending, tension and impact resistance. Additionally, for discussing the results an anatomical characterization of the White Bolaina wood fiber (length, diameter, wall thickness, lumen diameter and slenderness coefficient) and a chemical analysis of its components (extractives, holocellulose, lignin and ash) was carried out. Results allow to appreciate a direct relationship between the variable mixing ratio and the mainly physical properties, as well as between the variable particle size with respect to tension. Wood age did not represent a significant source of variability.

          Related collections

          Most cited references22

          • Record: found
          • Abstract: not found
          • Article: not found

          Biodegradable composites based on lignocellulosic fibers—An overview

            Bookmark
            • Record: found
            • Abstract: not found
            • Article: not found

            Development of bamboo-based polymer composites and their mechanical properties

              Bookmark
              • Record: found
              • Abstract: not found
              • Article: not found

              A comparison of compounding processes and wood type for wood fibre—PP composites

                Bookmark

                Author and article information

                Journal
                remcf
                Revista mexicana de ciencias forestales
                Rev. mex. de cienc. forestales
                Instituto Nacional de Investigaciones Forestales, Agrícolas y Pecuarias (México, Distrito Federal, Mexico )
                2007-1132
                February 2020
                : 11
                : 57
                : 4-31
                Affiliations
                [2] Lima orgnameUniversidad Nacional Agraria La Molina orgdiv1Departamento de Industrias Forestales orgdiv2Facultad de Ciencias Forestales Peru
                [1] Lima orgnameUniversidad Nacional Agraria La Molina Peru
                Article
                S2007-11322020000100004 S2007-1132(20)01105700004
                10.29298/rmcf.v11i57.621
                8d6c6c64-f743-4230-8a09-1fdd4dc109df

                This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

                History
                : 22 July 2019
                : 26 November 2019
                Page count
                Figures: 0, Tables: 0, Equations: 0, References: 44, Pages: 28
                Product

                SciELO Mexico

                Categories
                Artículo científico

                physical properties,materiales compuestos plástico madera,polypropylene,módulo de elasticidad,modulus of elasticity,polipropileno,wood plastic composites,Guazuma crinita Mart.,propiedades mecánicas,propiedades físicas,mechanical properties

                Comments

                Comment on this article