Formation of Hierarchical Cu-Doped CoSe2 Microboxes via Sequential Ion Exchange for High-Performance Sodium-Ion Batteries

Lithium transition metal phosphates have become of great interest as storage cathodes for rechargeable lithium batteries because of their high energy density, low raw materials cost, environmental friendliness and safety. Their key limitation has been extremely low electronic conductivity, until now believed to be intrinsic to this family of compounds. Here we show that controlled cation non-stoichiometry combined with solid-solution doping by metals supervalent to Li+ increases the electronic conductivity of LiFePO4 by a factor of approximately 10(8). The resulting materials show near-theoretical energy density at low charge/discharge rates, and retain significant capacity with little polarization at rates as high as 6,000 mA x g(-1). In a conventional cell design, they may allow development of lithium batteries with the highest power density yet.

Graphite, as the most common anode for commercial Li-ion batteries, has been reported to have a very low capacity when used as a Na-ion battery anode. It is well known that electrochemical insertion of Na(+) into graphite is significantly hindered by the insufficient interlayer spacing. Here we report expanded graphite as a Na-ion battery anode. Prepared through a process of oxidation and partial reduction on graphite, expanded graphite has an enlarged interlayer lattice distance of 4.3 Å yet retains an analogous long-range-ordered layered structure to graphite. In situ transmission electron microscopy has demonstrated that the Na-ion can be reversibly inserted into and extracted from expanded graphite. Galvanostatic studies show that expanded graphite can deliver a high reversible capacity of 284 mAh g(-1) at a current density of 20 mA g(-1), maintain a capacity of 184 mAh g(-1) at 100 mA g(-1), and retain 73.92% of its capacity after 2,000 cycles.

Sodium-ion batteries are emerging as a highly promising technology for large-scale energy storage applications. However, it remains a significant challenge to develop an anode with superior long-term cycling stability and high-rate capability. Here we demonstrate that the Na(+) intercalation pseudocapacitance in TiO2/graphene nanocomposites enables high-rate capability and long cycle life in a sodium-ion battery. This hybrid electrode exhibits a specific capacity of above 90 mA h g(-1) at 12,000 mA g(-1) (∼36 C). The capacity is highly reversible for more than 4,000 cycles, the longest demonstrated cyclability to date. First-principle calculations demonstrate that the intimate integration of graphene with TiO2 reduces the diffusion energy barrier, thus enhancing the Na(+) intercalation pseudocapacitive process. The Na-ion intercalation pseudocapacitance enabled by tailor-deigned nanostructures represents a promising strategy for developing electrode materials with high power density and long cycle life.