      Influence of Nitriding and Multiple Peening on Surface Characteristic of Tool Steel AISI D2 Translated title: Der Einfluss des Nitrierens und des Mehrfachstrahlens auf die Oberflächeneigenschaft des Werkzeugstahls X153CrMoV12

      Read this article at

      ScienceOpenPublisher
      Bookmark
          There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

          Abstract

          The purpose of this study is to clarify the effect of the combined treatment of nitriding and multi-stage peening on the friction and wear characteristics of tool steel AISI D2. In the measurement of the surface roughness, it was clarified that the size of the dimple changes by the multiple peening treatment when the nitriding treatment is not applied. It was indicated that the surface roughness increased by forming the Sn layer on the surface when the nitriding treatment was performed. It was revealed that the hardness increased significantly by applying multiple peening treatment after nitriding treatment in hardness measurement. In residual stress measurement, it was revealed that residual stress of about −1500 MPa is imparted by multiple peening treatment. In addition, it could be shown that higher residual stress is given after the nitriding treatment. It became obvious the friction coefficient of AISI D2 can be greatly reduced by nitriding multiple peening treatment. In addition, it was clarified that the friction coefficient can be reduced even with only the multiple peening treatment.

          Kurzfassung

          Der Zweck dieser Studie ist es, den Effekt der kombinierten Behandlung von Nitrieren und Mehrfachstrahlen auf die Reibungs- und Abriebeigenschaften von X153CrMoV12 zu klären. Bei der Messung der Oberflächenrauheit wurde gezeigt, dass sich die Größen der Vertiefungen um das Vielfache durch Mehrfachstrahlen ändern, wenn die Nitrierbehandlung nicht angewendet wird. Es konnte nachgewiesen werden, dass die Oberflächenrauheit durch Bilden der Sn-Schicht auf der Oberfläche anstieg, wenn die Nitrierbehandlung durchgeführt wurde. Zudem wurde beobachtet, dass die Härte durch Anwendung einer Mehrfachstrahlbehandlung nach der Nitrierbehandlung bei der Härtemessung signifikant anstieg. Bei der Eigenspannungsmessung wurde gezeigt, dass eine Druckeigenspannung von etwa −1500 MPa durch Mehrfachstrahlen erzeugt wird. Darüber hinaus wurde ersichtlich, dass nach der Nitrierbehandlung eine höhere Druckeigenspannung auftritt. Es konnte nachgewiesen werden, dass der Reibkoeffizient von X153CrMoV12 durch Nitrieren mit Mehrfachstrahlen stark verringert werden kann. Darüber hinaus war es nachweisbar möglich, den Reibkoeffizient auch nur mittels der Mehrfachstrahlbehandlung zu verringern.

          Related collections

          Most cited references 11

          • Record: found
          • Abstract: found
          • Article: not found

          Carbon plasma immersion ion implantation of nickel-titanium shape memory alloys.

          Nickel-titanium (NiTi) shape memory alloys possess super-elasticity in addition to the well-known shape memory effect and are potentially suitable for orthopedic implants. However, a critical concern is the release of harmful Ni ions from the implants into the living tissues. We propose to enhance the corrosion resistance and other surface and biological properties of NiTi using carbon plasma immersion ion implantation and deposition (PIII&D). Our corrosion and simulated body fluid tests indicate that either an ion-mixed amorphous carbon coating fabricated by PIII&D or direct carbon PIII can drastically improve the corrosion resistance and block the out-diffusion of Ni from the materials. Our tribological tests show that the treated surfaces are mechanically more superior and cytotoxicity tests reveal that both sets of plasma-treated samples favor adhesion and proliferation of osteoblasts.
            Bookmark
            • Record: found
            • Abstract: not found
            • Article: not found

            Effect of shot peening using ultra-fine particles on fatigue properties of 5056 aluminum alloy under rotating bending

              Bookmark
              • Record: found
              • Abstract: not found
              • Article: not found

              Influence of Fine Particle Bombarding on Various Characteristics of SUP10

               K Nambu,  K Matsuzaka,  N Egami (2010)
                Bookmark

                Author and article information

                Journal
                htme
                HTM Journal of Heat Treatment and Materials
                Carl Hanser Verlag
                1867-2493
                2194-1831
                9 April 2020
                : 75
                : 2
                : 97-104
                Affiliations
                1 Toyota Technological Institute, 2-12-1, Hisakata, Tenpaku-ku, Nagoya, Aichi, Japan
                2 Daido University, 10-3, Takiharu-cho, Minami-ku, Nagoya, Aichi, Japan
                Author notes
                3 knambu@ 123456toyota-ti.ac.jp (corresponding author/Kontakt)
                Article
                HT110407
                10.3139/105.110407
                © 2020, Carl Hanser Verlag, München
                Page count
                References: 12, Pages: 8
                Product
                Self URI (journal page): http://www.hanser-elibrary.com/loi/htme
                Categories
                Scientific Contributions/Fachbeiträge

                Comments

                Comment on this article