      Combined Hot Isostatic Pressing and Heat Treatment of Aluminum A356 Cast Alloys* Translated title: Heißisostatisches Pressen von Aluminiumgusslegierungen mit integrierter Wärmebehandlung

      Read this article at

      ScienceOpenPublisher
      Bookmark
          There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

          Abstract

          The mechanical and microstructural properties of aluminum A356 cast alloy are investigated as a function of hot isostatic pressing and heat treatment parameters. The combined hot isostatic pressing and heat treatment process leads to an improvement of mechanical properties when compared to regular hot isostatic pressing with no separate heat treatment. An oversaturated state with magnesium and silicon atoms dissolved in the aluminum matrix can be achieved by increasing the quenching rate to 6.9 K/s within the temperature range between 813 K and 473 K. Aging can be performed directly after hot isostatic pressing, without the necessity of a separate solution annealing step. Thereby, the overall processing costs could be reduced.

          Kurzfassung

          Die Forschungsarbeit zeigt die Möglichkeit auf, heißisostatisches Pressen und Lösungsglühen in einem Prozessschritt zu realisieren. Mit dem Gebrauch einer neuartigen Schnellkühlung integriert in einer heißisostatischen Presse konnten beim Absenken der Temperatur von 813 K auf 473 K Abschreckraten von bis zu 6,9 K/s erreicht werden. Die mikrostrukturelle sowie die mechanische Werkstoffcharakterisierung belegen eine mit dem Prozessschritt des heißisostatischen Pressens erreichte Einstellung eines übersättigten Mischkristalls. Die Auslagerungsbehandlung kann somit unmittelbar nach dem heißisostatischen Pressen ohne zusätzliches Lösungsglühen durchgeführt werden. Dadurch könnten die gesamten Herstellkosten gesenkt werden.

          Related collections

          Most cited references 25

          • Record: found
          • Abstract: not found
          • Article: not found

          The precipitation sequence in Al–Mg–Si alloys

            Bookmark
            • Record: found
            • Abstract: not found
            • Article: not found

            The crystal structure of the β″ phase in Al–Mg–Si alloys

              Bookmark
              • Record: found
              • Abstract: not found
              • Article: not found

              Fatigue behavior of A356-T6 aluminum cast alloys. Part I. Effect of casting defects

                Bookmark

                Author and article information

                Journal
                htme
                HTM Journal of Heat Treatment and Materials
                Carl Hanser Verlag
                1867-2493
                2194-1831
                15 June 2016
                : 71
                : 3
                : 117-124
                Affiliations
                1 Lehrstuhl für Werkstoffkunde und Werkstoffmechanik, Fakultät für Maschinenwesen, Technische Universität München, Boltzmannstr. 15, 85748 Garching, Germany
                2 AUDI AG, Technologieentwicklung Gießen, 85045 Ingolstadt
                3 Avure Technologies AB, Quintusvägen 2, 72166 Västerås, Sweden
                4 Lehrstuhl für Werkstoffkunde und Werkstoffmechanik, Fakultät für Maschinenwesen, Technische Universität München
                Author notes
                [*]

                Lecture held by Stephan Hafenstein at the HK2015, 71 st HeatTreatmentCongress, October 28–30, 2015, in Cologne.

                5 hafenstein@ 123456wkm.mw.tum.de (Corresponding author/Kontakt)
                Article
                HT110281
                10.3139/105.110281
                © 2016, Carl Hanser Verlag, München
                Page count
                References: 25, Pages: 8
                Product
                Self URI (journal page): http://www.hanser-elibrary.com/loi/htme
                Categories
                Fachbeiträge/Technical Contributions

                Comments

                Comment on this article