      Painéis de partículas aglomeradas de madeira de Pinus elliottii Engelm., poliestireno (PS) e polietileno tereftalato (PET) Translated title: Particleboards of Pinus elliottii Engelm. wood, polystyrene and polyethylene therephthalate particles

      research-article

      Read this article at

      Bookmark
          There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

          Abstract

          O objetivo deste trabalho foi avaliar as propriedades de painéis fabricados com partículas de madeira, poliestireno (PS) e polietileno tereftalato (PET). Foram utilizadas três proporções, em relação à massa seca de madeira, de poliestireno (0, 25 e 50%) e duas proporções de PET/PS (5/20 e 10/40%), combinadas com 50, 75 ou 100% de partículas de madeira de Pinus elliottii. Os painéis foram produzidos com adesivos à base de uréia-formaldeído ou de fenol-formaldeído, em três teores (0, 4 ou 6%) e três níveis de solução de poliestireno em tolueno (0 , 4 e 6%), todos calculados em relação à massa seca total dos painéis. Foram produzidos painéis de aproximadamente 400 x 400 x 10 mm, em camada única, com densidade aproximada de 0,6 g/cm³. Determinou-se a resistência dos painéis à tração perpendicular à superfície, à flexão estática (módulos de ruptura (MOR) e elasticidade (MOE)), ao arrancamento de parafusos, bem como a absorção de água e o inchamento em espessura, após 24 horas de imersão. Todas as propriedades mecânicas dos painéis foram superiores às exigidas pela norma ANSI/A 208.1-1993. Contudo, todos os painéis absorveram água em valores superiores àqueles normalmente observados em painéis comerciais. Apesar disto, o inchamento em espessura foi compatível com o dos painéis de partículas de madeira existentes no mercado. Os painéis nos quais se aplicou a solução de poliestireno foram, de modo geral, os que apresentaram os melhores valores para todas as propriedades.

          Translated abstract

          This work aimed determine the properties of wood particleboards containing particles of polystyrene (PS) and polyethylene therephthalate (PET). Three amounts of polystyrene (0, 25 and 50%), two amounts of PET/PS (5/20 and 10/40%), three amounts (0, 4 and 6%) of urea-formaldehyde or phenol-formaldehyde adhesive and three amounts of polystyrene in toluene solution (0, 4 and 6%), combined with 50, 75 or 100% of particles of Pinus elliottii wood were used. Layer boards measuring approximately 400 x 400 x 10 mm with density approximately equal to 0.60 g/cm³ were produced. Internal bond, rupture and elasticity modulus, screw withdrawal, water absorption and thickness swelling after 24 hours of immersion were determined. The mechanical properties of all the boards were superior to the established by ANSI/A 208.1-1993 standard. All wood/plastic particleboards absorbed more water than those observed in commercial boards. However, the observed thickness swelling was quite similar to the values of commercial wood particleboards. Boards in which the solution of polystyrene was applied presented, in general, the best values for all the properties.

          Related collections

          Most cited references1

          • Record: found
          • Abstract: not found
          • Article: not found

          Mat-formed wood particleboard: specification ANSI A 208.1.1993

          (1993)
            Bookmark

            Author and article information

            Contributors
            Role: ND
            Role: ND
            Role: ND
            Role: ND
            Journal
            rarv
            Revista Árvore
            Rev. Árvore
            Sociedade de Investigações Florestais (Viçosa )
            1806-9088
            April 2004
            : 28
            : 2
            : 257-266
            Affiliations
            [1 ] Universidade Federal de Viçosa Brazil
            Article
            S0100-67622004000200012
            10.1590/S0100-67622004000200012
            aee865b7-ae68-44c2-8a3c-29bfa357bd7f

            http://creativecommons.org/licenses/by/4.0/

            History
            Product

            SciELO Brazil

            Self URI (journal page): http://www.scielo.br/scielo.php?script=sci_serial&pid=0100-6762&lng=en
            Categories
            FORESTRY

            Forestry
            Particleboards,polystyrene,polyethylene therephthalate,solution of polystyrene in toluene,Painéis de partículas,poliestireno,polietileno tereftalato,solução de poliestireno em tolueno

            Comments

            Comment on this article