      Effect of multi-walled carbon nanotube addition on the microstructures and mechanical properties of Ti(C,N)-based cermets

      research-article

      Read this article at

      ScienceOpenPublisher
      Bookmark
          There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

          Abstract

          The surface modification of multi-walled carbon nanotubes (MWCNTs) was carried out using plasma treatment. The microstructures of the prepared cermets with different additions of MWCNTs were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX), and X-ray diffraction (XRD). Mechanical properties such as transverse rupture strength (TRS), fracture toughness ( K IC), and hardness (HRA) were measured. The results showed that some reactive groups were successfully modified on the surface of MWCNTs, resulting in the improvement of dispersibility. Most of the amorphous carbons and impurities were peeled from the MWCNTs. Increasing MWCNT addition decreased the dissolution of tungsten, titanium, and molybdenum in the binder phase. The cermet with 0.5 wt% MWCNT addition showed the highest TRS and fracture toughness. The strengthening mechanisms were attributed to the finer grain size, the homogeneous microstructure, and the higher volume fraction of binder phase in the binder. The toughening mechanisms were characterized by bridging and pulling-out.

          Related collections

          Author and article information

          Journal
          Journal of Advanced Ceramics
          Journal of Advanced Ceramics
          Tsinghua University Press (Tsinghua University, Beijing 100084, China )
          2226-4108
          05 March 2018
          : 07
          : 01
          : 58-63
          Affiliations
          College of Chemistry and Materials Science, Longyan University, Longyan 364000, China
          Author notes
          * Corresponding author. E-mail: 365103755@ 123456qq.com
          Article
          2226-4108-07-01-58
          10.1007/s40145-017-0256-y

          This work is licensed under a Creative Commons Attribution 4.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

          Product
          Self URI: Publisher
          Categories
          Research Article

          Comments

          Comment on this article