Nanostructural hierarchy increases the strength of aluminium alloys

There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

Abstract

Increasing the strength of metallic alloys while maintaining formability is an interesting challenge for enabling new generations of lightweight structures and technologies. In this paper, we engineer aluminium alloys to contain a hierarchy of nanostructures and possess mechanical properties that expand known performance boundaries-an aerospace-grade 7075 alloy exhibits a yield strength and uniform elongation approaching 1 GPa and 5%, respectively. The nanostructural architecture was observed using novel high-resolution microscopy techniques and comprises a solid solution, free of precipitation, featuring (i) a high density of dislocations, (ii) subnanometre intragranular solute clusters, (iii) two geometries of nanometre-scale intergranular solute structures and (iv) grain sizes tens of nanometres in diameter. Our results demonstrate that this novel architecture offers a design pathway towards a new generation of super-strong materials with new regimes of property-performance space.

Related collections

Most cited references 49

Record: found
Abstract: not found
Article: not found

Bulk nanostructured materials from severe plastic deformation

R.Z Valiev, R.K Islamgaliev, I.V Alexandrov (2000)

0 comments Cited 401 times – based on 0 reviews      Review now

Bookmark

Record: found
Abstract: found
Article: not found

High tensile ductility in a nanostructured metal.

Yinmin Wang, Mingwei Chen, Fenghua Zhou … (2002)

Nanocrystalline metals--with grain sizes of less than 100 nm--have strengths exceeding those of coarse-grained and even alloyed metals, and are thus expected to have many applications. For example, pure nanocrystalline Cu (refs 1-7) has a yield strength in excess of 400 MPa, which is six times higher than that of coarse-grained Cu. But nanocrystalline materials often exhibit low tensile ductility at room temperature, which limits their practical utility. The elongation to failure is typically less than a few per cent; the regime of uniform deformation is even smaller. Here we describe a thermomechanical treatment of Cu that results in a bimodal grain size distribution, with micrometre-sized grains embedded inside a matrix of nanocrystalline and ultrafine (<300 nm) grains. The matrix grains impart high strength, as expected from an extrapolation of the Hall-Petch relationship. Meanwhile, the inhomogeneous microstructure induces strain hardening mechanisms that stabilize the tensile deformation, leading to a high tensile ductility--65% elongation to failure, and 30% uniform elongation. We expect that these results will have implications in the development of tough nanostructured metals for forming operations and high-performance structural applications including microelectromechanical and biomedical systems.