This paper presents a technical feasibility analysis of the incorporation of Rice Husk Ash (RHA), Sludge from Water Treatment Station (SWTS) and Wood Ash (WA) in clay for the mass used in ceramic coating. The methodology involved analyzing the technological properties of various compositions. Samples were prepared for pressing, with compositions from 0 to 50% waste and 50 to 100% clay. The sintering was carried out in a muffle furnace. The properties studied were: solubility and leaching (environmental characterization), water absorption and rupture strength modulus. It was concluded that the best condition was the use of up to 25% of the residuals at temperatures of 1000 ºC, 1100 ºC and 1150 ºC.
Este trabalho tem como objetivo a análise da viabilidade técnica na incorporação de Cinza de Casca de Arroz (CCA), Lodo de Estação de Tratamento de Água (LETA) e Cinza de Lenha (CL) para massa cerâmica utilizada para cerâmica de revestimento. A metodologia consistiu na análise das propriedades tecnológicas de várias composições. Foram confeccionados corpos-de-prova por prensagem, com composições de 0 a 50% de resíduo e 50 a 100% de argila. A queima foi feita em forno tipo mufla. As propriedades analisadas foram solubilidade e lixiviação (caracterização ambiental), absorção de água e módulo de ruptura a flexão. Como resultados, concluiu-se ser viável a utilização de até 25% dos resíduos nas temperaturas de 1000ºC, 1100ºC e 1150ºC.