Molten salt-assisted synthesis of nitrogen-vacancy crystalline graphitic carbon nitride with tunable band structures for efficient photocatalytic overall water splitting

Overall water splitting based on particulate photocatalysts is an easily constructed and cost-effective technology for the conversion of abundant solar energy into clean and renewable hydrogen energy on a large scale. Overall water splitting based on particulate photocatalysts is an easily constructed and cost-effective technology for the conversion of abundant solar energy into clean and renewable hydrogen energy on a large scale. This promising technology can be achieved in a one-step excitation system using a single photocatalyst or via a Z-scheme process based on a pair of photocatalysts. Ideally, such photocatalysis will proceed with charge separation and transport unaffected by recombination and trapping, and surface catalytic processes will not involve undesirable reactions. This review summarizes the basics of overall water splitting via both one-step excitation and Z-scheme processes, with a focus on standard methods of determining photocatalytic performance. Various surface engineering strategies applied to photocatalysts, such as cocatalyst loading, surface morphology control, surface modification and surface phase junctions, have been developed to allow efficient one-step excitation overall water splitting. In addition, numerous visible-light-responsive photocatalysts have been successfully utilized as H 2 -evolution or O 2 -evolution photocatalysts in Z-scheme overall water splitting. Prototype particulate immobilization systems with photocatalytic performances comparable to or drastically higher than those of particle suspension systems suggest the exciting possibility of the large-scale production of low-cost renewable solar hydrogen.

Isolated single-atom platinum (Pt) embedded in the sub-nanoporosity of 2D g-C3 N4 as a new form of co-catalyst is reported. The highly stable single-atom co-catalyst maximizes the atom efficiency and alters the surface trap states of g-C3 N4 , leading to significantly enhanced photocatalytic H2 evolution activity, 8.6 times higher than that of Pt nanoparticles and up to 50 times that for bare g-C3 N4 .