Effect of carbon anode production parameters on anode cracking

Graphical abstract

Carbon anodes are used in the electrolytic production of aluminum. The quality of anodes is directly related to the production cost, carbon and energy consumption, and environmental emissions. It is desired that the anodes have high density, low porosity/cracks, low electrical resistivity as well as low air and CO ₂ reactivities. Low resistivity of anodes reduces energy required to produce aluminum during electrolysis. The presence of cracks and pores increases the anode electrical resistivity. Therefore, it is important to know how and when the pores and cracks form during the anode production so that the necessary actions could be taken to prevent their formation. A study was carried out to investigate the effect of different anode production parameters such as anode composition, type of raw material used, time and top-former bellow pressure of vibro-compactor, green anode cooling medium, and heating rate used during baking on the crack formation. The anodes are fabricated at the carbon laboratory of University of Quebec at Chicoutimi (UQAC) and characterized by measuring their properties (density, electrical resistivity, and surface crack density). The anode properties, hence the anode quality, were correlated with the anode production parameters. Also, their tomographic analysis was carried out to visualize and quantify the internal cracks.