Photoinduced Absorption Spectroscopy of CoPi on BiVO4: The Function of CoPi during Water Oxidation

Water oxidation is a critical step in water splitting to make hydrogen fuel. We report the solution synthesis, structural/compositional characterization, and oxygen evolution reaction (OER) electrocatalytic properties of ~2-3 nm thick films of NiO(x), CoO(x), Ni(y)Co(1-y)O(x), Ni(0.9)Fe(0.1)O(x), IrO(x), MnO(x), and FeO(x). The thin-film geometry enables the use of quartz crystal microgravimetry, voltammetry, and steady-state Tafel measurements to study the electrocatalytic activity and electrochemical properties of the oxides. Ni(0.9)Fe(0.1)O(x) was found to be the most active water oxidation catalyst in basic media, passing 10 mA cm(-2) at an overpotential of 336 mV with a Tafel slope of 30 mV dec(-1) with oxygen evolution reaction (OER) activity roughly an order of magnitude higher than IrO(x) control films and similar to the best known OER catalysts in basic media. The high activity is attributed to the in situ formation of layered Ni(0.9)Fe(0.1)OOH oxyhydroxide species with nearly every Ni atom electrochemically active. In contrast to previous reports that showed synergy between Co and Ni oxides for OER catalysis, Ni(y)Co(1-y)O(x) thin films showed decreasing activity relative to the pure NiO(x) films with increasing Co content. This finding is explained by the suppressed in situ formation of the active layered oxyhydroxide with increasing Co. The high OER activity and simple synthesis make these Ni-based catalyst thin films useful for incorporating with semiconductor photoelectrodes for direct solar-driven water splitting or in high-surface-area electrodes for water electrolysis.

The mechanism of the oxygen evolution reaction (OER) by catalysts prepared by electrodepositions from Co(2+) solutions in phosphate electrolytes (Co-Pi) was studied at neutral pH by electrokinetic and (18)O isotope experiments. Low-potential electrodepositions enabled the controlled preparation of ultrathin Co-Pi catalyst films (<100 nm) that could be studied kinetically in the absence of mass transport and charge transport limitations to the OER. The Co-Pi catalysts exhibit a Tafel slope approximately equal to 2.3 × RT/F for the production of oxygen from water in neutral solutions. The electrochemical rate law exhibits an inverse first order dependence on proton activity and a zeroth order dependence on phosphate for [Pi] ≥ 0.03 M. In the absence of phosphate buffer, the Tafel slope is increased ∼3-fold and the overall activity is greatly diminished. Together, these electrokinetic studies suggest a mechanism involving a rapid, one electron, one proton equilibrium between Co(III)-OH and Co(IV)-O in which a phosphate species is the proton acceptor, followed by a chemical turnover-limiting process involving oxygen-oxygen bond coupling.

Metal oxides are generally very stable in aqueous solutions and cheap, but their photochemical activity is usually limited by poor charge carrier separation. Here we show that this problem can be solved by introducing a gradient dopant concentration in the metal oxide film, thereby creating a distributed n(+)-n homojunction. This concept is demonstrated with a low-cost, spray-deposited and non-porous tungsten-doped bismuth vanadate photoanode in which carrier-separation efficiencies of up to 80% are achieved. By combining this state-of-the-art photoanode with an earth-abundant cobalt phosphate water-oxidation catalyst and a double- or single-junction amorphous Si solar cell in a tandem configuration, stable short-circuit water-splitting photocurrents of ~4 and 3 mA cm(-2), respectively, are achieved under 1 sun illumination. The 4 mA cm(-2) photocurrent corresponds to a solar-to-hydrogen efficiency of 4.9%, which is the highest efficiency yet reported for a stand-alone water-splitting device based on a metal oxide photoanode.