One-step solvothermal synthesis of hierarchically porous nanostructured CdS/TiO2 heterojunction with higher visible light photocatalytic activity

Unique spindle-shaped nanoporous anatase TiO(2) mesocrystals with a single-crystal-like structure and tunable sizes were successfully fabricated on a large scale through mesoscale assembly in the tetrabutyl titanate-acetic acid system without any additives under solvothermal conditions. A complex mesoscale assembly process involving slow release of soluble species from metastable solid precursors for the continuous formation of nascent anatase nanocrystals, oriented aggregation of tiny anatase nanocrystals, and entrapment of in situ produced butyl acetate as a porogen was put forward for the formation of the anatase mesocrystals. It was revealed that the acetic acid molecules played multiple key roles during the nonhydrolytic processing of the [001]-oriented, single-crystal-like anatase mesocrystals. The obtained nanoporous anatase mesocrystals exhibited remarkable crystalline-phase stability (i.e., the pure phase of anatase can be retained after being annealed at 900 °C) and improved performance as anode materials for lithium ion batteries, which could be largely attributed to the intrinsic single-crystal-like nature as well as high porosity of the nanoporous mesocrystals.

Porous silica, niobia, and titania with three-dimensional structures patterned over multiple length scales were prepared by combining micromolding, polystyrene sphere templating, and cooperative assembly of inorganic sol-gel species with amphiphilic triblock copolymers. The resulting materials show hierarchical ordering over several discrete and tunable length scales ranging from 10 nanometers to several micrometers. The respective ordered structures can be independently modified by choosing different mold patterns, latex spheres, and block copolymers. The examples presented demonstrate the compositional and structural diversities that are possible with this simple approach.