Synthesis of silver nanoparticles with different shapes

The antibacterial effect and mechanism of action of a silver ion solution that was electrically generated were investigated for Staphylococcus aureus and Escherichia coli by analyzing the growth, morphology, and ultrastructure of the bacterial cells following treatment with the silver ion solution. Bacteria were exposed to the silver ion solution for various lengths of time, and the antibacterial effect of the solution was tested using the conventional plate count method and flow cytometric (FC) analysis. Reductions of more than 5 log(10) CFU/ml of both S. aureus and E. coli bacteria were confirmed after 90 min of treatment with the silver ion solution. Significant reduction of S. aureus and E. coli cells was also observed by FC analysis; however, the reduction rate determined by FC analysis was less than that determined by the conventional plate count method. These differences may be attributed to the presence of bacteria in an active but nonculturable (ABNC) state after treatment with the silver ion solution. Transmission electron microscopy showed considerable changes in the bacterial cell membranes upon silver ion treatment, which might be the cause or consequence of cell death. In conclusion, the results of the present study suggest that silver ions may cause S. aureus and E. coli bacteria to reach an ABNC state and eventually die.

The concept of shape-controlled synthesis is discussed by investigating the growth mechanisms for silver nanocubes, nanowires, and nanospheres produced through a polymer-mediated polyol process. Experimental parameters, such as the concentration of AgNO(3) (the precursor to silver), the molar ratio between poly(vinylpyrrolidone) (PVP, the capping agent) and AgNO(3), and the strength of chemical interaction between PVP and various crystallographic planes of silver, were found to determine the crystallinity of seeds (e.g., single crystal versus decahedral multiply twinned particles). In turn, the crystallinity of a seed and the extent of the PVP coverage on the seed were both instrumental in controlling the morphology of final product. The ability to generate silver nanostructures with well-defined morphologies provides a great opportunity to experimentally and systematically study the relationship between their properties and geometric shapes.