Simultaneous H2Generation and Biomass Upgrading in Water by an Efficient Noble-Metal-Free Bifunctional Electrocatalyst

Access to clean, affordable and reliable energy has been a cornerstone of the world's increasing prosperity and economic growth since the beginning of the industrial revolution. Our use of energy in the twenty-first century must also be sustainable. Solar and water-based energy generation, and engineering of microbes to produce biofuels are a few examples of the alternatives. This Perspective puts these opportunities into a larger context by relating them to a number of aspects in the transportation and electricity generation sectors. It also provides a snapshot of the current energy landscape and discusses several research and development opportunities and pathways that could lead to a prosperous, sustainable and secure energy future for the world.

The efficiency of many energy storage technologies, such as rechargeable metal-air batteries and hydrogen production from water splitting, is limited by the slow kinetics of the oxygen evolution reaction (OER). We found that Ba(0.5)Sr(0.5)Co(0.8)Fe(0.2)O(3-δ) (BSCF) catalyzes the OER with intrinsic activity that is at least an order of magnitude higher than that of the state-of-the-art iridium oxide catalyst in alkaline media. The high activity of BSCF was predicted from a design principle established by systematic examination of more than 10 transition metal oxides, which showed that the intrinsic OER activity exhibits a volcano-shaped dependence on the occupancy of the 3d electron with an e(g) symmetry of surface transition metal cations in an oxide. The peak OER activity was predicted to be at an e(g) occupancy close to unity, with high covalency of transition metal-oxygen bonds.

Fe plays a critical, but not yet understood, role in enhancing the activity of the Ni-based oxygen evolution reaction (OER) electrocatalysts. We report electrochemical, in situ electrical, photoelectron spectroscopy, and X-ray diffraction measurements on Ni(1-x)Fe(x)(OH)2/Ni(1-x)Fe(x)OOH thin films to investigate the changes in electronic properties, OER activity, and structure as a result of Fe inclusion. We developed a simple method for purification of KOH electrolyte that uses precipitated bulk Ni(OH)2 to absorb Fe impurities. Cyclic voltammetry on rigorously Fe-free Ni(OH)2/NiOOH reveals new Ni redox features and no significant OER current until >400 mV overpotential, different from previous reports which were likely affected by Fe impurities. We show through controlled crystallization that β-NiOOH is less active for OER than the disordered γ-NiOOH starting material and that previous reports of increased activity for β-NiOOH are due to incorporation of Fe-impurities during the crystallization process. Through-film in situ conductivity measurements show a >30-fold increase in film conductivity with Fe addition, but this change in conductivity is not sufficient to explain the observed changes in activity. Measurements of activity as a function of film thickness on Au and glassy carbon substrates are consistent with the hypothesis that Fe exerts a partial-charge-transfer activation effect on Ni, similar to that observed for noble-metal electrode surfaces. These results have significant implications for the design and study of Ni(1-x)Fe(x)OOH OER electrocatalysts, which are the fastest measured OER catalysts under basic conditions.