A carbon modified MnO2 nanosheet array as a stable high-capacitance supercapacitor electrode

Electrochemical supercapacitors can deliver high levels of electrical power and offer long operating lifetimes, but their energy storage density is too low for many important applications. Pseudocapacitive transition-metal oxides such as MnO(2) could be used to make electrodes in such supercapacitors, because they are predicted to have a high capacitance for storing electrical charge while also being inexpensive and not harmful to the environment. However, the poor conductivity of MnO(2) (10(-5)-10(-6) S cm(-1)) limits the charge/discharge rate for high-power applications. Here, we show that hybrid structures made of nanoporous gold and nanocrystalline MnO(2) have enhanced conductivity, resulting in a specific capacitance of the constituent MnO(2) (~1,145 F g(-1)) that is close to the theoretical value. The nanoporous gold allows electron transport through the MnO(2), and facilitates fast ion diffusion between the MnO(2) and the electrolytes while also acting as a double-layer capacitor. The high specific capacitances and charge/discharge rates offered by such hybrid structures make them promising candidates as electrodes in supercapacitors, combining high-energy storage densities with high levels of power delivery.

By use of the membrane-templated synthesis route, hydrous RuO2 (RuO2.xH2O) nanotubular arrayed electrodes were successfully synthesized by means of the anodic deposition technique. The desired three-dimensional mesoporous architecture of RuO2.xH2O nanotubular arrayed electrodes with annealing in air at 200 degrees C for 2 h simultaneously maintained the facility of electrolyte penetration, the ease of proton exchange/diffusion, and the metallic conductivity of crystalline RuO2, exhibiting unexpectedly ultrahigh power characteristics with its frequency "knee" reaching ca. 4.0-7.8 kHz, 20-40 times better than that of RuO2 single crystalline, arrayed nanorods. The specific power and specific energy of annealed RuO2.xH2O nanotubes measured at 0.8 V and 4 kHz is equal to 4320 kW kg-1 and 7.5 W h kg-1, respectively, demonstrating the characteristics of next generation supercapacitors.