Electrocaloric and pyroelectric properties of 0.75Pb(Mg1∕3Nb2∕3)O3–0.25PbTiO3 single crystals

An applied electric field can reversibly change the temperature of an electrocaloric material under adiabatic conditions, and the effect is strongest near phase transitions. This phenomenon has been largely ignored because only small effects (0.003 K V^-1) have been seen in bulk samples such as Pb0.99Nb0.02(Zr0.75Sn0.20Ti0.05)0.98O3 and there is no consensus on macroscopic models. Here we demonstrate a giant electrocaloric effect (0.48 K V^-1) in 300 nm sol-gel PbZr0.95Ti0.05O3 films near the ferroelectric Curie temperature of 222oC. We also discuss a solid state device concept for electrical refrigeration that has the capacity to outperform Peltier or magnetocaloric coolers. Our results resolve the controversy surrounding macroscopic models of the electrocaloric effect and may inspire ab initio calculations of electrocaloric parameters and thus a targeted search for new materials.

Synchrotron x-ray powder diffraction measurements have been performed on unpoled ceramic samples of (1-x)PbMg(1/3)Nb(2/3)O3-xPbTiO3 (PMN-xPT) with 30%<= x<= 39% as a function of temperature around the morphotropic phase boundary (MPB), which is the line separating the rhombohedral and tetragonal phases in the phase diagram. The experiments have revealed very interesting features previously unknown in this or related systems. The sharp and well-defined diffraction profiles observed at high and intermediate temperatures in the cubic and tetragonal phases, respectively, are in contrast to the broad features encountered at low temperatures. These peculiar characteristics, which are associated with the monoclinic phase of MC-type previously reported by Kiat et al and Singh et al., can only be interpreted as multiple coexisting structures with MC as the major component. An analysis of the diffraction profiles has allowed us to properly characterize the PMN-xPT phase diagram and to determine the stability region of the monoclinic phase, which extends from x= 31% to x= 37% at 20 K. The complex lansdcape of observed phases points to an energy balance between the different PMN-xPT phases which is intrinsically much more delicate than that of related systems such as PbZr(1-x)TixO3 or (1-x)PbZn(1/3)Nb(1/3)O3-xPbTiO3. These observations are in good accord with an optical study of x= 33% by Xu et al., who observed monoclinic domains with several different polar directions coexisting with rhombohedral domains, in the same single crystal.