The purposes of this study were to evaluate the shear bond strength of a new collapsible monocrystalline bracket (Inspire, Ormco, Orange, Calif) and compare it with another collapsible ceramic bracket (Clarity, 3M Unitek, Monrovia, Calif) and a metal bracket; to examine the modes of failure after shear bond strength testing; and to observe the tooth surface after debonding the ceramic brackets with pliers. One hundred extracted human premolars were selected for bonding. Three types of brackets and 2 orthodontic adhesives (Transbond XT, 3M Unitek; and Enlight, Ormco) were used. After bonding, all samples were placed in a distilled water bath at 37 degrees C for 24 hours. The shear bond strength of 60 samples was measured, and the remaining 40 samples with ceramic brackets were debonded with pliers. No statistically significant differences in bond strengths among the different combinations of brackets and adhesives were found (P > .05). The mode of failure after debonding by either shear bond strength testing or with pliers was predominantly at the bracket/adhesive interface in all groups. Enamel and bracket fractures were noted in 2 and 5 of 20 samples for Inspire, and 1 and 0 of 20 samples for Clarity after debonding with pliers. Bond strength and mode of failure of Inspire were similar to those of Clarity, but the risk of bracket fracture after debonding for Inspire was greater.