Highly Efficient Rubber-to-Stainless Steel Bonding by Nanometer-Thin Cross-linked Polymer Brushes

There is no author summary for this article yet. Authors can add summaries to their articles on ScienceOpen to make them more accessible to a non-specialist audience.

Abstract

Stainless steel (SS) surfaces were grafted with poly(glycidyl methacrylate) (PGMA) brushes that were post-modified using allylamine, diallylamine, and propylamine as reagents. Likewise, poly[2-(diethylamino)ethyl methacrylate] brushes were synthesized. All samples were compression molded with uncured ethylene-propylene-diene M-class rubber and dicumyl peroxide and vulcanized for 12 min at 170 °C. The efficiency of the novel bonding solution was evaluated through peel experiments. Two parameters, the fracture toughness ( ) and the cohesive-to-adhesive fracture ratio (A r), were calculated to evaluate the strength and the performance of the coupling, respectively. For the nanometer-thin PGMA films modified with allylamine, in particular, full cohesive fracture was obtained. The obtained values of (15.4 ± 1.1 N mm–1) and A r (1.00 ± 0.01) matched those obtained for a micrometer-thick commercial bonding agent. Cross-linking of polymer brushes by intermolecular reactions by the primary amines proved to have a significant impact on the type of fracture (cohesive/adhesive) and the performance of the adhesives.

Related collections

Most cited references 34

Record: found
Abstract: found
Article: not found

Diminishing catalyst concentration in atom transfer radical polymerization with reducing agents.

Krzysztof Matyjaszewski, Wojciech Jakubowski, Ke Min … (2006)

The concept of initiators for continuous activator regeneration (ICAR) in atom transfer radical polymerization (ATRP) is introduced, whereby a constant source of organic free radicals works to regenerate the Cu(I) activator, which is otherwise consumed in termination reactions when used at very low concentrations. With this technique, controlled synthesis of polystyrene and poly(methyl methacrylate) (Mw/Mn < 1.2) can be implemented with catalyst concentrations between 10 and 50 ppm, where its removal or recycling would be unwarranted for many applications. Additionally, various organic reducing agents (derivatives of hydrazine and phenol) are used to continuously regenerate the Cu(I) activator in activators regenerated by electron transfer (ARGET) ATRP. Controlled polymer synthesis of acrylates (Mw/Mn < 1.2) is realized with catalyst concentrations as low as 50 ppm. The rational selection of suitable Cu complexing ligands {tris[2-(dimethylamino)ethyl]amine (Me6TREN) and tris[(2-pyridyl)methyl]amine (TPMA)} is discussed in regards to specific side reactions in each technique (i.e., complex dissociation, acid evolution, and reducing agent complexation). Additionally, mechanistic studies and kinetic modeling are used to optimize each system. The performance of the selected catalysts/reducing agents in homo and block (co)polymerizations is evaluated.